At what level is H2 considered to be more critical in cracking
At what level is H2 considered to be more critical in cracking
Open 410In general terms which of the following would require the highest preheat if all other factors were the same as per ISO/BS EN 1011?
In general terms which of the following would require the highest preheat if all other factors were the same as per ISO/BS EN 1011?
Open 411Which of the following microstructure is critical to the likely formation of hydrogen cracks?
Which of the following microstructure is critical to the likely formation of hydrogen cracks?
Open 412The correct joint preparaton is very important since it decides the volume of weld metal to be used,,high volumes of weld metal deposited can
The correct joint preparaton is very important since it decides the volume of weld metal to be used,,high volumes of weld metal deposited can
Open 413Basic electrodes are often sold vacuum packed. The reason is?
Basic electrodes are often sold vacuum packed. The reason is?
Open 414Post heating of weld joints is carried out in order to
Post heating of weld joints is carried out in order to
Open 415In oxy fuel cutting when cutting thin metals which fuel is used
In oxy fuel cutting when cutting thin metals which fuel is used
Open 416Which polarity is normally used for TIG welding of stainless steel?
Which polarity is normally used for TIG welding of stainless steel?
Open 417CEV of C-Mn
CEV of C-Mn
Open 418Ar-N2 is used for welding
Ar-N2 is used for welding
Open 419Cast and helix related to
Cast and helix related to
Open 420What is the greatest advantage of radiographic inspection over ultrasonic inspection?
What is the greatest advantage of radiographic inspection over ultrasonic inspection?
Open 421The most common reason why finish grinding of a butt weld is specified to be an application standard is to:
The most common reason why finish grinding of a butt weld is specified to be an application standard is to:
Open 422A welder’s qualification certificate issued to BS EN 287 or ASME IX may have to be withdrawn if
A welder’s qualification certificate issued to BS EN 287 or ASME IX may have to be withdrawn if
Open 423For TIG welding austenitic stainless steel there is a requirement for a high standard of cleanliness. What is the main reason for this?
For TIG welding austenitic stainless steel there is a requirement for a high standard of cleanliness. What is the main reason for this?
Open 424Side bend tests for butt weld joints are
Side bend tests for butt weld joints are
Open 425Which of the following is an effective way of reducing residual stresses caused by welding?
Which of the following is an effective way of reducing residual stresses caused by welding?
Open 426Electrodes designated E46 4 B (to BS EN 499) have been left out overnight on the workbench in a fabrication workshop. What is the best course of action?
Electrodes designated E46 4 B (to BS EN 499) have been left out overnight on the workbench in a fabrication workshop. What is the best course of...
Open 427For SAW which of the following has most effect on the finished profile?
For SAW which of the following has most effect on the finished profile?
Open 428The strength of a fillet weld is controlled by
The strength of a fillet weld is controlled by
Open 429Changing a welding procedure ‘essential’ variable beyond the specified limits during production welding will require
Changing a welding procedure ‘essential’ variable beyond the specified limits during production welding will require
Open 430Steels that have good toughness at very low temperature are alloyed with
Steels that have good toughness at very low temperature are alloyed with
Open 431The main purpose of a ‘slope in’ control in TIG welding is to
The main purpose of a ‘slope in’ control in TIG welding is to
Open 432On welding quenched and tempered steels which of the following would increase the risk of weld HAZ cracking?
On welding quenched and tempered steels which of the following would increase the risk of weld HAZ cracking?
Open